half-cell potential
英 [hɑːf sel pəˈtenʃl]
美 [hæf sel pəˈtenʃl]
半电池电位; 半电池电势
双语例句
- The corrosion of the reinforcing steel in concrete is an electrochemical process, and the half-cell potential is on of the utmost characters in estimating the condition of the rebar.
混凝土中钢筋的腐蚀是一个电化学过程，而半电池电位是判断钢筋状态的重要依据。 - Based on practical application conditions, half-cell potential method, concrete resistance measurement, linear polarization resistance method and etc.
根据现场的实际应用情况，最常用的方法有半电池电位法、混凝土电阻率检测法、直流线性极化电阻法、交流阻抗法以及地质雷达法等。 - Get the corrosion rate by the experience formula from the half-cell potential.
依据线性极化经验公式，利用半电池电位法检测的电位结果，亦可估算钢筋锈蚀的速率。 - In this study, sodium chloride doped reinforced concrete specimens were subjected to electrochemical chloride extraction after cured at humid atmosphere for 100 days and the half-cell potential ( HCP) and corrosion current of steel bars in concrete electrochemical chloride extraction ( ECE) were determined.
研究了掺盐钢筋混凝土在不同水化龄期及经电化学除盐处理后的自腐蚀电位和腐蚀速率，并跟踪了断电后钢筋的自腐蚀电位和腐蚀速率随时间的变化。 - The reinforcement surface corrosion states of concrete samples of nine types of technical conditions are judged by half-cell potential, A.
用半电池电位法、交流阻抗法、时间电位法判断9种技术条件的混凝土试件中钢筋表面腐蚀状态。 - Evaluation of reinforcement corrosion in reinforced concrete member by half-cell potential method
用半电池电位评估钢筋混凝土构件中钢筋腐蚀状态 - The relationships between the water-cement ratio of concrete, relative humidity, corrosion state of the reinforcement and the half-cell potential of the reinforcement of a reinforced concrete member are analyzed.
分析了混凝土水灰比、相对湿度、钢筋腐蚀状态与钢筋混凝土构件内钢筋的半电池电位的关系。 - Based on the indoor test results of reinforced concrete samples and measured results of some members of Zhanjiang Dock and Tianjin Dock, China, the half-cell potential scope for evaluation of the reinforcement corrosion state of reinforced concrete members of coastal harbors in China is preliminarily presented.
并通过室内钢筋混凝土试件试验及对湛江、天津港码头部分构件的检测，初步给出了适合我国海港钢筋混凝土结构中判别钢筋腐蚀的半电池电位的范围。 - The results showed that the half-cell potential method can only be used in the qualitative detection of corrosion.
研究表明，自然电位法的适用性仅局限在对混凝土中钢筋锈蚀的定性检测，不能应用于定量测量。